- 熔體流動速率 [g/10min]: 0.04
- 密度 [g/cm3]: 0.949
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in3 | ASTM D1505 |
| Thickness | 12.7 microns | 0.500 mil | |
| Melt Flow | 0.040 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.040 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| High Load Melt Index | 8.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 8.0 g/10 min @Load 47.6 lb, Temperature 374 °F | Condition F; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 330 % | 330 % | ASTM D882 |
| Film Elongation at Break, TD | 455 % | 455 % | ASTM D882 |
| Elmendorf Tear Strength MD | 18 g | 18 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 35 g | 35 g | ASTM D1922 |
| Dart drop Test | 300 g | 0.662 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 60.0 MPa | 8700 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 31.0 MPa | 4500 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 131 °C | 268 °F | DSC |
| Processing Properties | Metric | English | Comments |
| Blow-up Ratio (BUR) | 4.0 | 4.0 | |