- 熔體流動速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.954
- 拉伸強度 [MPa]: 26.0
- 彎曲模量 [MPa]: 1.15
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in3 | ASTM D792 |
| Melt Flow | 20 g/10 min @Load 2.16 kg | 20 g/10 min @Load 4.76 lb | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 57 | 57 | ASTM D2240 |
| Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | >= 300 % | >= 300 % | ASTM D638 |
| Flexural Modulus | 1.15 GPa | 167 ksi | ASTM D790 |
| Izod Impact, Unnotched | 0.300 J/cm | 0.562 ft-lb/in | ASTM D256 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 175 - 245 °C | 347 - 473 °F | |
| Mold Temperature | 10.0 - 40.0 °C | 50.0 - 104 °F | |