- 熔體流動速率 [g/10min]: 0.4
- 密度 [g/cm3]: 0.954
- 拉伸強(qiáng)度 [MPa]: 27.0
- 彎曲模量 [MPa]: 1.25
- 熱變形溫度 [℃]: 70.0
- 脆化溫度 [℃]: -100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in3 | ASTM D792 |
| Environmental Stress Crack Resistance | 50 hour | 50 hour | F50; ASTM D1693 B |
| Melt Flow | 0.40 g/10 min @Load 2.16 kg | 0.40 g/10 min @Load 4.76 lb | ASTM D1238 |
| High Load Melt Index | 29 g/10 min @Load 21.6 kg | 29 g/10 min @Load 47.6 lb | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ASTM D638 |
| Elongation at Break | 1140 % | 1140 % | ASTM D638 |
| Flexural Modulus | 1.25 GPa | 181 ksi | ASTM D790 |
| Crush Resistance | 50.0 kg | 110 lb (mass) | 41g Boston Round Quart Bottle; ASTM D2659 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 120 μm/m-°C | 66.7 μin/in-°F | ASTM D969 |
| Melting Point | 135 °C | 275 °F | Equate Test Method |
| Crystallization Temperature | 112 °C | 234 °F | Equate Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D1525 |
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Zone 1 | 175 - 180 °C | 347 - 356 °F | |
| Zone 2 | 185 - 190 °C | 365 - 374 °F | |
| Zone 3 | 185 - 190 °C | 365 - 374 °F | |
| Zone 4 | 185 - 190 °C | 365 - 374 °F | |
| Adapter Temperature | 185 - 190 °C | 365 - 374 °F | |
| Die Temperature | 185 - 190 °C | 365 - 374 °F | |
| Melt Temperature | 200 - 215 °C | 392 - 419 °F | Intermittent Machines |
| 215 °C | 419 °F | 90 RPM | |
| 220 °C | 428 °F | 130 RPM | |
| Head Temperature | 185 - 190 °C | 365 - 374 °F | |
- 關(guān)鍵詞:
- HDPE
- 供應(yīng)
- Equate EMDA-6200 HDPE Blow Molding Resin