- 熔體流動速率 [g/10min]: 7.0
- 密度 [g/cm3]: 0.961
- 拉伸強度 [MPa]: 29.0
- 彎曲模量 [MPa]: 1.28
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.961 g/cc | 0.0347 lb/in3 | ASTM D792 |
| Environmental Stress Crack Resistance | <= 10 hour | <= 10 hour | F50, Condition A, ASTM D1693, 100% Igepal |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
| Elongation at Break | 1200 % | 1200 % | ASTM D638 |
| Flexural Modulus | 1.28 GPa | 186 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 129 °C | 264 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 215 °C | 338 - 419 °F | |