- 熔體流動速率 [g/10min]: 0.28
- 密度 [g/cm3]: 0.96
- 拉伸強度 [MPa]: 31.5
- 彎曲模量 [MPa]: 1.31
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in3 | ASTM D792 |
| Environmental Stress Crack Resistance | 75 hour | 75 hour | F50, Condition A, ASTM D1693, 100% Igepal |
| Melt Flow | 0.28 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.28 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 67 | 67 | ASTM D2240 |
| Tensile Strength, Yield | 31.5 MPa | 4570 psi | ASTM D638 |
| Elongation at Break | 1000 % | 1000 % | ASTM D638 |
| Flexural Modulus | 1.31 GPa | 190 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 160 - 205 °C | 320 - 401 °F | |