- 熔體流動速率 [g/10min]: 4.8
- 密度 [g/cm3]: 0.947
- 拉伸強度 [MPa]: 22.0
- 彎曲模量 [MPa]: 0.862
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.947 g/cc | 0.0342 lb/in3 | ASTM D792 |
| Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | 1000 % | 1000 % | ASTM D638 |
| Flexural Modulus | 0.862 GPa | 125 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 122 °C | 252 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 215 °C | 338 - 419 °F | |