- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.945
- 拉伸強度 [MPa]: 22.0
- 彎曲模量 [MPa]: 1.03
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in3 | ASTM D1505 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | >= 400 % | >= 400 % | ASTM D638 |
| Flexural Modulus | 1.03 GPa | 149 ksi | ASTM D790 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.33 @Frequency 100000 Hz | 2.33 @Frequency 100000 Hz | ASTM D1531 |
| Dielectric Strength | 20.0 kV/mm @Thickness 3.17 mm | 508 kV/in @Thickness 0.125 in | ASTM D149 |
| Dissipation Factor | >= 0.00010 @Frequency 100000 Hz | >= 0.00010 @Frequency 100000 Hz | ASTM D1531 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 218 - 274 °C | 424 - 525 °F | Stock Temperature |