- 熔體流動速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.963
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.963 g/cc | 0.0348 lb/in3 | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 24.0 MPa | 3480 psi | Cast Film; ASTM D638 |
| Film Tensile Strength at Yield, TD | 25.0 MPa | 3630 psi | Cast Film; ASTM D638 |
| Film Elongation at Break, MD | 625 % | 625 % | Cast film; ASTM D638 |
| Film Elongation at Break, TD | 700 % | 700 % | Cast film; ASTM D638 |
| Elmendorf Tear Strength MD | 55 g | 55 g | Cast Film; ASTM D1922 |
| Elmendorf Tear Strength TD | 65 g | 65 g | Cast Film; ASTM D1922 |
| Elmendorf Tear Strength, MD | 2.17 g/micron | 55.0 g/mil | 1 mil; Cast Film; ASTM D1922 |
| Elmendorf Tear Strength, TD | 2.56 g/micron | 65.0 g/mil | 1 mil; Cast Film; ASTM D1922 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.33 @Frequency 100000 Hz | 2.33 @Frequency 100000 Hz | ASTM D1531 |
| Dielectric Strength | 20.0 kV/mm @Thickness 3.17 mm | 508 kV/in @Thickness 0.125 in | ASTM D149 |
| Dissipation Factor | >= 0.00010 @Frequency 100000 Hz | >= 0.00010 @Frequency 100000 Hz | ASTM D1531 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 232 °C | 379 - 450 °F | Stock Temperature |