- 熔體流動速率 [g/10min]: 0.28
- 密度 [g/cm3]: 0.947
- 彎曲模量 [MPa]: 1.103
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.947 g/cc | 0.0342 lb/in3 | ASTM D1505 |
| Moisture Vapor Transmission | 0.200 cc-mm/m2-24hr-atm | 0.508 cc-mil/100 in2-24hr-atm | ASTM E96 |
| Oxygen Transmission | 59.0 cc-mm/m2-24hr-atm | 150 cc-mil/100 in2-24hr-atm | ASTM D1434 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.28 g/10 min | 0.28 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 24.0 MPa | 3480 psi | Blown film; ASTM D882 |
| 26.0 MPa | 3770 psi | Blown film; ASTM D882 | |
| Film Elongation at Break, MD | 480 % | 480 % | Blown film; ASTM D638 |
| Film Elongation at Break, TD | 640 % | 640 % | Blown film; ASTM D638 |
| Flexural Modulus | 1.103 GPa | 160.0 ksi | ASTM D790 |
| Elmendorf Tear Strength MD | 23 g | 23 g | Blown Film; ASTM D1922 |
| Elmendorf Tear Strength TD | 330 g | 330 g | Blown Film; ASTM D1922 |
| Elmendorf Tear Strength, MD | 0.906 g/micron | 23.0 g/mil | 1 mil; Blown Film; ASTM D1922 |
| Elmendorf Tear Strength, TD | 13.0 g/micron | 330 g/mil | 1 mil; Blown Film; ASTM D1922 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.33 @Frequency 100000 Hz | 2.33 @Frequency 100000 Hz | ASTM D1531 |
| Dielectric Strength | 20.0 kV/mm @Thickness 3.17 mm | 508 kV/in @Thickness 0.125 in | ASTM D149 |
| Dissipation Factor | >= 0.00010 @Frequency 100000 Hz | >= 0.00010 @Frequency 100000 Hz | ASTM D1531 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 216 °C | 379 - 421 °F | Stock Temperature |