- 熔體流動速率 [g/10min]: 50.0
- 密度 [g/cm3]: 0.95
- 拉伸強度 [MPa]: 19.0
- 彎曲強度 [MPa]: 12.0
- 彎曲模量 [MPa]: 0.862
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in3 | |
| Viscosity | 33000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 33000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 40000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 40000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 95000 cP @Shear Rate 300 1/s, Temperature 190 °C | 95000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 50 g/10 min @Load 2.16 kg | 50 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8.5. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | |
| Elongation at Break | 190 % | 190 % | |
| Modulus of Elasticity | 0.565 GPa | 81.9 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.862 GPa | 125 ksi | |
| Izod Impact Resistance | 2.70 J/cm2 | 12.8 ft-lb/in2 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 119 °C | 246 °F | |