- 熔體流動速率 [g/10min]: 17.0
- 密度 [g/cm3]: 0.95
- 拉伸強度 [MPa]: 18.6
- 彎曲強度 [MPa]: 13.1
- 彎曲模量 [MPa]: 0.862
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in3 | |
| Viscosity | 75000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 75000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 140000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 140000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 200000 cP @Shear Rate 300 1/s, Temperature 190 °C | 200000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 17 g/10 min @Load 2.16 kg | 17 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 13.1 MPa | 1900 psi | |
| Tensile Strength, Yield | 18.6 MPa | 2700 psi | |
| Elongation at Break | 660 % | 660 % | |
| Modulus of Elasticity | 0.593 GPa | 86.0 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.862 GPa | 125 ksi | |
| Izod Impact Resistance | 8.01 J/cm2 | 38.1 ft-lb/in2 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 123 °C | 253 °F | |