- 熔體流動速率 [g/10min]: 60.0
- 密度 [g/cm3]: 0.952
- 拉伸強度 [MPa]: 21.0
- 彎曲強度 [MPa]: 10.0
- 彎曲模量 [MPa]: 0.869
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | |
| Melt Flow | 60 g/10 min @Load 2.16 kg | 60 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8.5. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | |
| Elongation at Break | 225 % | 225 % | |
| Modulus of Elasticity | 0.641 GPa | 93.0 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.869 GPa | 126 ksi | |
| Izod Impact Resistance | 1.60 J/cm2 | 7.61 ft-lb/in2 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 122 °C | 252 °F | |