- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.963
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.963 g/cc | 0.0348 lb/in3 | |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg | 5.0 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8.1. |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 27.5 MPa | 3990 psi | |
| Film Tensile Strength at Yield, TD | 28.3 MPa | 4100 psi | |
| Film Elongation at Break, MD | 595 % | 595 % | |
| Film Elongation at Break, TD | 650 % | 650 % | |
| Secant Modulus, MD | 0.472 GPa | 68.5 ksi | Film value |
| Secant Modulus, TD | 0.572 GPa | 83.0 ksi | Film value |
| Elmendorf Tear Strength MD | 40 g | 40 g | |
| Elmendorf Tear Strength TD | 118 g | 118 g | |
| Elmendorf Tear Strength, MD | 1.60 g/micron | 40.6 g/mil | |
| Elmendorf Tear Strength, TD | 4.70 g/micron | 119 g/mil | |
| Dart Drop | 1.60 g/micron | 40.6 g/mil | |
| Film Tensile Strength at Break, MD | 35.6 MPa | 5160 psi | |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 130 °C | 266 °F | |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | |
| Gloss | 85 % | 85 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 274 °C | 525 °F | Film extrusion temperature |