- 熔體流動速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.952
- 拉伸強度 [MPa]: 19.3
- 彎曲強度 [MPa]: 19.0
- 彎曲模量 [MPa]: 0.889
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | |
| Viscosity | 105000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 105000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 270000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 270000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 480000 cP @Shear Rate 300 1/s, Temperature 190 °C | 480000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg | 4.0 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 19.0 MPa | 2760 psi | |
| Tensile Strength, Yield | 19.3 MPa | 2800 psi | |
| Elongation at Break | 600 % | 600 % | |
| Modulus of Elasticity | 0.607 GPa | 88.0 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.889 GPa | 129 ksi | |
| Izod Impact Resistance | 17.6 J/cm2 | 83.8 ft-lb/in2 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 123 °C | 253 °F | |