- 密度 [g/cm3]: 0.947
- 拉伸強(qiáng)度 [MPa]: 23.4
- 彎曲模量 [MPa]: 0.800
- 熱變形溫度 [℃]: 60.0
- 脆化溫度 [℃]: -72.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.947 g/cc | 0.0342 lb/in3 | ASTM D792 |
| Melt Index of Compound | 50 g/10 min @Load 2.16 kg, Temperature 190 °C | 50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 48 | 48 | Molded and tested in accordance with ASTM D4976; ASTM D2240 |
| Tensile Strength at Break | 22.1 MPa | 3200 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Tensile Strength, Yield | 23.4 MPa | 3400 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 10 % | 10 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 0.800 GPa | 116 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
| Tensile Impact Strength | 42.0 kJ/m2 | 20.0 ft-lb/in2 | Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 127 °C | 261 °F | Dow Method (DSC) |
| Crystallization Temperature | 115 °C | 239 °F | Dow Method (DSC) |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Vicat Softening Point | 120 °C | 248 °F | ASTM D1525 |
| Brittleness Temperature | -72.8 °C | -99.0 °F | Molded and tested in accordance with ASTM D4976; ASTM D746 |