- 密度 [g/cm3]: 0.961
- 拉伸強度 [MPa]: 29.6
- 彎曲模量 [MPa]: 1.24
- 熱變形溫度 [℃]: 78.9
- 脆化溫度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.961 g/cc | 0.0347 lb/in3 | ASTM D792 |
| ESCR 100% Igepal? | 20 hour @Temperature 50.0 °C | 20 hour @Temperature 122 °F | F50; Molded and tested in accordance with ASTM D4976; ASTM D1693 |
| High Load Melt Index | 47 g/10 min @Load 21.6 kg, Temperature 190 °C | 47 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Melt Index of Compound | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 58 | 58 | Molded and tested in accordance with ASTM D4976; ASTM D2240 |
| Tensile Strength at Break | 29.0 MPa | 4200 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Tensile Strength, Yield | 29.6 MPa | 4300 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 1000 % | 1000 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 1.24 GPa | 180 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
| Tensile Impact Strength | 126 kJ/m2 | 60.0 ft-lb/in2 | Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 134 °C | 273 °F | Dow Method (DSC) |
| Crystallization Temperature | 120 °C | 248 °F | Dow Method (DSC) |
| Deflection Temperature at 0.46 MPa (66 psi) | 78.9 °C | 174 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Vicat Softening Point | 130 °C | 266 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | Molded and tested in accordance with ASTM D4976; ASTM D746 |