- 密度 [g/cm3]: 0.952
- 拉伸強度 [MPa]: 17.2
- 彎曲模量 [MPa]: 1.00
- 熱變形溫度 [℃]: 68.9
- 脆化溫度 [℃]: -20.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D792 |
| Melt Index of Compound | 66 g/10 min @Load 2.16 kg, Temperature 190 °C | 66 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 59 | 59 | Molded and tested in accordance with ASTM D4976; ASTM D2240 |
| Tensile Strength at Break | 28.3 MPa | 4100 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Tensile Strength, Yield | 17.2 MPa | 2500 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 10 % | 10 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Yield | 1.0 % | 1.0 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 1.00 GPa | 145 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
| Tensile Impact Strength | 63.0 kJ/m2 | 30.0 ft-lb/in2 | Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 128 °C | 262 °F | Dow Method (DSC) |
| Crystallization Temperature | 116 °C | 241 °F | Dow Method (DSC) |
| Deflection Temperature at 0.46 MPa (66 psi) | 68.9 °C | 156 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Vicat Softening Point | 122 °C | 252 °F | ASTM D1525 |
| Brittleness Temperature | -20.0 °C | -4.00 °F | Molded and tested in accordance with ASTM D4976; ASTM D746 |