- 熔體流動速率 [g/10min]: 11.5
- 密度 [g/cm3]: 0.952
- 拉伸強度 [MPa]: 25.5
- 彎曲模量 [MPa]: 1.24
- 脆化溫度 [℃]: -70.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| Melt Flow | 11.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 11.5 g/10 min @Load 4.76 lb, Temperature 374 °F | Procedure A Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.5 MPa | 3700 psi | Type IV bar at chs 2 in per min; ASTM D638 |
| Elongation at Break | 700 % | 700 % | ASTM D638 |
| Flexural Modulus | 1.24 GPa | 180 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.6 °C | <= -95.0 °F | ASTM D746 |