- 熔體流動速率 [g/10min]: 46.0
- 密度 [g/cm3]: 0.952
- 彎曲模量 [MPa]: 1.07
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| Melt Flow | 46 - 50 g/10 min @Load 2.16 kg, Temperature 230 °C | 46 - 50 g/10 min @Load 4.76 lb, Temperature 446 °F | Procedure A Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 24.8 MPa | 3600 psi | chs 2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 1.07 GPa | 155 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |