- 熔體流動速率 [g/10min]: 4.2
- 密度 [g/cm3]: 0.952
- 彎曲模量 [MPa]: 1.07
- 脆化溫度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| Melt Flow | 4.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.2 g/10 min @Load 4.76 lb, Temperature 374 °F | Procedure A Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 26.2 MPa | 3800 psi | ASTM D638 |
| Elongation at Break | 1200 % | 1200 % | ASTM D638 |
| Flexural Modulus | 1.07 GPa | 155 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Tensile Impact Strength | 71.4 kJ/m2 | 34.0 ft-lb/in2 | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | ASTM D746 |