- 熔體流動速率 [g/10min]: 0.1
- 拉伸強度 [MPa]: 33.9
- 彎曲模量 [MPa]: 1.123
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| 23.6 g/10 min @Load 2.16 kg, Temperature 230 °C | 23.6 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 33.9 MPa | 4920 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Break | 8.7 % | 8.7 % | chs 2.0 in/min; ASTM D638 |
| Flexural Strength | 29.8 MPa | 4320 psi | chs 0.05 in/min; ASTM D790 |
| Flexural Modulus | 1.123 GPa | 162.9 ksi | chs 0.05 in/min; ASTM D790 |