- 密度 [g/cm3]: 0.8
- 彎曲強(qiáng)度 [MPa]: 22.1
- 彎曲模量 [MPa]: 1.57
- 熱變形溫度 [℃]: 50.0
- 脆化溫度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.800 g/cc | 0.0289 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | 25 hour | 25 hour | F50; ASTM D1693 |
| >= 500 hour | >= 500 hour | F50; ASTM D2561 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 69 | 69 | ASTM D2240 |
| Tensile Strength, Ultimate | 22.1 MPa | 3200 psi | ASTM D638 |
| Flexural Strength | 27.6 MPa | 4000 psi | ASTM D790 |
| Flexural Modulus | 1.57 GPa | 228 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 50.0 °C | 122 °F | ASTM D648 |
| Vicat Softening Point | 129 °C | 264 °F | ASTM D1525 |
| Brittleness Temperature | -76.1 °C | -105 °F | ASTM D746 |