- 熔體流動速率 [g/10min]: 0.27
- 密度 [g/cm3]: 0.95
- 拉伸強度 [MPa]: 26.9
- 彎曲模量 [MPa]: 1.03
- 脆化溫度 [℃]: -100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in3 | ASTM D1505 |
| Apparent Bulk Density | 0.590 g/cc | 0.0213 lb/in3 | ASTM D1895 |
| Melt Flow | 0.27 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.27 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
| Elongation at Break | >= 500 % | >= 500 % | ASTM D638 |
| Flexural Modulus | 1.03 GPa | 149 ksi | 1% Secant; ASTM D 790 |
| Tensile Impact Strength | 115 kJ/m2 | 54.7 ft-lb/in2 | S bar; ASTM D 1822 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 124 °C | 255 °F | ASTM D1525 |
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D746 |