- 熔體流動速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.94
- 拉伸強度 [MPa]: 19.0
- 彎曲強度 [MPa]: 31.0
- 彎曲模量 [MPa]: 0.790
- 脆化溫度 [℃]: -59.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 2000 hour @Temperature 50.0 °C | >= 2000 hour @Temperature 122 °F | F50, Cond. B.; ASTM D1693 |
| >= 5000 hour @Temperature 100 °C | >= 5000 hour @Temperature 212 °F | F50 Cond. C; ASTM D 1693 | |
| Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.20 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ASTM D2240 |
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638 |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.790 GPa | 115 ksi | 3 pt. secant. ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 120 °C | 248 °F | ASTM D1525 |
| Brittleness Temperature | <= -59.0 °C | <= -74.2 °F | ASTM D746 |