- 熔體流動速率 [g/10min]: 0.8
- 彎曲強度 [MPa]: 14.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.921 - 0.925 g/cc | 0.921 - 0.925 g/cc | ASTM D1505 |
| Melt Flow | 0.80 - 1.2 g/10 min @Load 2.61 kg, Temperature 190 °C | 0.80 - 1.2 g/10 min @Load 5.75 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 14.7 MPa | 2130 psi | 500mm/min; ASTM D638 |
| Film Elongation at Break, MD | 300 % | 300 % | 500mm/min, Ultimate; ASTM D638 |
| Film Elongation at Break, TD | 550 % | 550 % | 500mm/min, Ultimate; ASTM D638 |
| Elongation at Break | 600 % | 600 % | 500 mm/min, Ultimate; ASTM D638 |
| 2% Secant Modulus | 1.25 GPa | 181 ksi | 500mm/min; ASTM D638 |
| Elmendorf Tear Strength MD | 450 g | 450 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 200 g | 200 g | ASTM D1922 |
| Dart drop Test | 75.0 g | 0.165 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 26.5 MPa | 3840 psi | 500mm/min, Ultimate; ASTM D638 |
| Film Tensile Strength at Break, TD | 24.5 MPa | 3550 psi | 500mm/min, Ultimate; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 95 % | 95 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 105 °C | 221 °F | 10°C/min; ASTM D3418 |