- 熔體流動(dòng)速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.98
- 缺口沖擊強(qiáng)度: 0.38
- 彎曲強(qiáng)度 [MPa]: 15.0
- 彎曲模量 [MPa]: 0.430
- 熱變形溫度 [℃]: 50.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | LATI | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | LATI | ||
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ISO 527 | ||
| Flexural Modulus | 0.430 GPa | 62.4 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.380 J/cm @Temperature -40.0 °C | 0.712 ft-lb/in @Temperature -40.0 °F | ASTM D256 | ||
| 1.50 J/cm @Temperature -20.0 °C | 2.81 ft-lb/in @Temperature -4.00 °F | ASTM D256 | |||
| 5.00 J/cm @Temperature 23.0 °C | 9.37 ft-lb/in @Temperature 73.4 °F | ASTM D256 | |||
| Charpy Impact Unnotched | >= 30.0 J/cm2 @Temperature -20.0 °C | >= 143 ft-lb/in2 @Temperature -4.00 °F | DIN 53453 | ||
| >= 30.0 J/cm2 @Temperature -40.0 °C | >= 143 ft-lb/in2 @Temperature -40.0 °F | DIN 53453 | |||
| >= 30.0 J/cm2 @Temperature 23.0 °C | >= 143 ft-lb/in2 @Temperature 73.4 °F | DIN 53453 | |||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | 100 ohm | 100 ohm | IEC 93 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 50.0 °C | 122 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 38.0 °C | 100 °F | ASTM D648 | ||
| Vicat Softening Point | 52.0 °C | 126 °F | 50°C/h 50N; ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 200 - 220 °C | 392 - 428 °F | |||
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |||
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Temperature can be reduced when using vacuum ovens. | ||
| Dry Time | >= 3 hour | >= 3 hour | Drying time can be reduced when using vacuum ovens. | ||
| Descriptive Properties | |||||
| Injection Speed | medium | ||||