- 熔體流動(dòng)速率 [g/10min]: 7.5
- 拉伸強(qiáng)度 [MPa]: 8.83
- 彎曲模量 [MPa]: 0.196
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.918 g/cc | 0.918 g/cc | ASTM D1505 |
| Water Vapor Transmission | 20.0 g/m2/day @Pressure 0.101 MPa | 1.29 g/100 in2/day @Pressure 14.7 psi | ASTM D393 |
| Melt Flow | 7.5 g/10 min @Load 2.61 kg, Temperature 190 °C | 7.5 g/10 min @Load 5.75 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 43 | 43 | ASTM D2240 |
| Tensile Strength at Break | 11.5 MPa | 1670 psi | 200mm/min; ASTM D638 |
| Tensile Strength, Yield | 8.83 MPa | 1280 psi | 200 mm/min; ASTM D638 |
| Elongation at Break | 550 % | 550 % | 200 mm/min; ASTM D638 |
| Flexural Modulus | 0.196 GPa | 28.4 ksi | 200mm/min; ASTM D790 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 107 °C | 225 °F | 10°C/min; DSC |