- 熔體流動速率 [g/10min]: 4.5
- 拉伸強度 [MPa]: 9.32
- 彎曲模量 [MPa]: 0.196
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.918 g/cc | 0.918 g/cc | ASTM D1505 |
| Water Vapor Transmission | 20.0 g/m2/day @Pressure 0.101 MPa | 1.29 g/100 in2/day @Pressure 14.7 psi | ASTM D393 |
| Melt Flow | 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 44 | 44 | ASTM D2240 |
| Tensile Strength at Break | 13.0 MPa | 1890 psi | 200mm/min; ASTM D638 |
| Tensile Strength, Yield | 9.32 MPa | 1350 psi | 200 mm/min; ASTM D638 |
| Elongation at Break | 540 % | 540 % | 200 mm/min; ASTM D638 |
| Flexural Modulus | 0.196 GPa | 28.4 ksi | 200mm/min; ASTM D790 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 107 °C | 225 °F | 10°C/min; DSC |