- 熔體流動(dòng)速率 [g/10min]: 1.5
- 密度 [g/cm3]: 0.93
- 拉伸強(qiáng)度 [MPa]: 14.0
- 彎曲強(qiáng)度 [MPa]: 12.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in3 | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 1.5 g/10 min | 1.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 | 60 | ASTM D2240 |
| Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Modulus of Elasticity | 0.380 GPa | 55.1 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.300 GPa | 43.5 ksi | ASTM D882 |
| Secant Modulus, TD | 0.380 GPa | 55.1 ksi | ASTM D882 |
| Dart Drop | 1.97 g/micron | 50.0 g/mil | ASTM D1709 |
| Dart drop Test | 50.0 g | 0.110 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 23.0 MPa | 3340 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 16.0 MPa | 2320 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 106 °C | 223 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 70 % | 70 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 182 - 194 °C | 360 - 381 °F | |