- 熔體流動速率 [g/10min]: 5.5
- 密度 [g/cm3]: 0.922
- 拉伸強度 [MPa]: 10.0
- 彎曲強度 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in3 | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 5.5 g/10 min | 5.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 52 | 52 | ASTM D2240 |
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D638 |
| Film Elongation at Break, MD | 275 % | 275 % | ASTM D882 |
| Film Elongation at Break, TD | 400 % | 400 % | ASTM D882 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Modulus of Elasticity | 0.242 GPa | 35.1 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.159 GPa | 23.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.186 GPa | 27.0 ksi | ASTM D882 |
| Dart Drop | 1.77 g/micron | 45.0 g/mil | ASTM D1709 |
| Dart drop Test | 45.0 g | 0.0992 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 17.0 MPa | 2470 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 14.0 MPa | 2030 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 96.0 °C | 205 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 78 % | 78 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 143 - 154 °C | 289 - 309 °F | |