- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.92
- 拉伸強度 [MPa]: 10.0
- 彎曲強度 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in3 | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50 | 50 | ASTM D2240 |
| Tensile Strength, Ultimate | 11.0 MPa | 1600 psi | ASTM D638 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D638 |
| Film Elongation at Break, MD | 325 % | 325 % | ASTM D882 |
| Film Elongation at Break, TD | 425 % | 425 % | ASTM D882 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Modulus of Elasticity | 0.221 GPa | 32.1 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.166 GPa | 24.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.173 GPa | 25.1 ksi | ASTM D882 |
| Dart Drop | 3.35 - 3.94 g/micron | 85.0 - 100 g/mil | ASTM D1709 |
| Dart drop Test | 85.0 - 100 g | 0.187 - 0.221 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 20.0 MPa | 2900 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 16.0 MPa | 2320 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Gloss | 55 % | 55 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 171 - 182 °C | 340 - 360 °F | |