- 熔體流動速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.924
- 拉伸強度 [MPa]: 10.0
- 彎曲強度 [MPa]: 14.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in3 | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.80 g/10 min | 0.80 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 53 | 53 | ASTM D2240 |
| Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D638 |
| Film Elongation at Break, MD | 150 % | 150 % | ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 |
| Elongation at Break | 650 % | 650 % | ASTM D638 |
| Modulus of Elasticity | 0.276 GPa | 40.0 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.207 GPa | 30.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.242 GPa | 35.1 ksi | ASTM D882 |
| Dart Drop | 3.94 g/micron | 100 g/mil | ASTM D1709 |
| Dart drop Test | 100 g | 0.221 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 31.0 MPa | 4500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 21.0 MPa | 3050 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.5 % | 5.5 % | ASTM D1003 |
| Gloss | 65 % | 65 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 182 - 194 °C | 360 - 381 °F | |