- 熔體流動速率 [g/10min]: 38.0
- 密度 [g/cm3]: 0.922
- 拉伸強度 [MPa]: 12.8
- 脆化溫度 [℃]: -25.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in3 | ASTM D1505 |
| Melt Flow | 38 g/10 min | 38 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 41 | 41 | ASTM D2280 |
| Tensile Strength at Break | 8.96 MPa | 1300 psi | Crosshead Speed - 20 in/min; ASTM D638 |
| Tensile Strength, Yield | 12.8 MPa | 1850 psi | Crosshead Speed - 20 in/min; ASTM D638 |
| Elongation at Yield | 13 % | 13 % | ASTM D638 |
| 1% Secant Modulus | 228 MPa | 33000 psi | Crosshead Speed - 1/2 in/min; ASTM D790 |
| 2% Secant Modulus | 0.186 GPa | 27.0 ksi | Crosshead Speed - 1/2 in/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 86.0 °C | 187 °F | ASTM D1525 |
| Brittleness Temperature | -25.0 °C | -13.0 °F | F50, Test method has been found useful for specification purposes, but does not necessarily indicate the lowest temperature at which the material may be used.; ASTM D746 |