- 熔體流動(dòng)速率 [g/10min]: 25.0
- 密度 [g/cm3]: 0.922
- 拉伸強(qiáng)度 [MPa]: 12.2
- 脆化溫度 [℃]: -35.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in3 | ASTM D1505 | ||
| Melt Flow | 25 g/10 min | 25 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 44 | 44 | ASTM D2280 | ||
| Tensile Strength at Break | 8.48 MPa | 1230 psi | Crosshead Speed - 20 in/min; ASTM D638 | ||
| Tensile Strength, Yield | 12.2 MPa | 1770 psi | Crosshead Speed - 20 in/min; ASTM D638 | ||
| Elongation at Yield | 14 % | 14 % | Crosshead Speed - 20 in/min; ASTM D638 | ||
| 1% Secant Modulus | 221 MPa | 32000 psi | Crosshead Speed - 1/2 in/min; ASTM D790 | ||
| 2% Secant Modulus | 0.179 GPa | 26.0 ksi | Crosshead Speed - 1/2 in/min; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 92.0 °C | 198 °F | ASTM D1525 | ||
| Brittleness Temperature | -35.0 °C | -31.0 °F | F50, Test method has been found useful for specification purposes, but does not necessarily indicate the lowest temperature at which the material may be used.; ASTM D746 | ||
| Descriptive Properties | |||||
| Antioxidant | Low | ||||
| Slip | None | ||||