- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.931
- 彎曲模量 [MPa]: 0.386
- 熱變形溫度 [℃]: 53.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.931 g/cc | 0.0336 lb/in3 | ASTM D1505 |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 59 | 59 | ASTM D2240 |
| Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D638 |
| Elongation at Break | >= 500 % | >= 500 % | ASTM D638 |
| Flexural Modulus | 0.386 GPa | 56.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 53.0 °C | 127 °F | ASTM D648 |
| Vicat Softening Point | 105 °C | 221 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |