- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in3 | ASTM D1505 | ||
| Thickness | 31.8 microns | 1.25 mil | 2:1 BUR; 25 mil die gap | ||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 12.4 MPa | 1800 psi | Molded; ASTM D638 | ||
| Film Elongation at Break, MD | 200 % | 200 % | ASTM D882 | ||
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 | ||
| Elongation at Break | 650 % | 650 % | Molded; ASTM D638 | ||
| Elmendorf Tear Strength MD | 350 g | 350 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 70 g | 70 g | ASTM D1922 | ||
| Dart drop Test | 110 g | 0.243 lb | F50; ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 22.1 MPa | 3200 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 15.9 MPa | 2300 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 183 MPa | 26500 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 221 MPa | 32000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 85.0 °C | 185 °F | ASTM D1525 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 177 °C | 350 °F | |||
| Descriptive Properties | |||||
| Antiblock | None | ||||
| Slip | None | ||||