- 熔體流動速率 [g/10min]: 0.4
- 密度 [g/cm3]: 0.93
- 拉伸強度 [MPa]: 16.5
- 彎曲模量 [MPa]: 0.494
- 熱變形溫度 [℃]: 48.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in3 | ASTM D1505 |
| Melt Flow | 0.40 g/10 min | 0.40 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
| Tensile Strength, Yield | 16.5 MPa | 2400 psi | ASTM D638 |
| Elongation at Break | 660 % | 660 % | ASTM D638 |
| Tensile Modulus | 0.483 GPa | 70.0 ksi | 1% Secant; ASTM D638 |
| Flexural Modulus | 0.494 GPa | 71.6 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ASTM D648 |
| Vicat Softening Point | 107 °C | 225 °F | ASTM D1525 |