- 熔體流動速率 [g/10min]: 200.0
- 拉伸強度 [MPa]: 8.0
- 彎曲模量 [MPa]: 0.100
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.915 g/cc | 0.915 g/cc | ISO 1183 |
| Melt Flow | 200 g/10 min @Load 2.16 kg, Temperature 190 °C | 200 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 42 | 42 | ISO 868/A |
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ISO 527 |
| Flexural Modulus | 0.100 GPa | 14.5 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 102 °C | 216 °F | Internal method |
| Vicat Softening Point | 72.0 °C @Load 1.00 kg | 162 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= 0.000 °C | <= 32.0 °F | ASTM D746 |