- 熔體流動速率 [g/10min]: 8.0
- 拉伸強度 [MPa]: 12.0
- 彎曲模量 [MPa]: 0.200
- 脆化溫度 [℃]: -65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.924 g/cc | 0.924 g/cc | ISO 1183 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50 | 50 | ISO 868/A |
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | ISO 527 |
| Flexural Modulus | 0.200 GPa | 29.0 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 112 °C | 234 °F | Internal method |
| Vicat Softening Point | 92.0 °C @Load 1.00 kg | 198 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | ASTM D746 |