- 熔體流動速率 [g/10min]: 3.5
- 脆化溫度 [℃]: -75.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.924 g/cc | 0.924 g/cc | ISO 1183 |
| Thickness | 18.0 - 50.0 microns | 0.709 - 1.97 mil | Recommended |
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | ISO 527-3 |
| Film Elongation at Break, MD | 300 % | 300 % | ISO 527-3 |
| Film Elongation at Break, TD | 600 % | 600 % | ISO 527-3 |
| Coefficient of Friction, Dynamic | 0.11 | 0.11 | ISO 8295 |
| Elmendorf Tear Strength, MD | 8.152 g/micron | 207.1 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 5.6045 g/micron | 142.35 g/mil | ISO 6383-2 |
| Dart drop Test | 105 g | 0.232 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 23.0 MPa | 3340 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 190 MPa | 27600 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 200 MPa | 29000 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 114 °C | 237 °F | Internal method |
| Vicat Softening Point | 94.0 °C @Load 1.00 kg | 201 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.5 % | 6.5 % | ISO 14782 |
| Gloss | 70 % | 70 % | 45°; ASTM D2457 |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |