- 熔體流動速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.905
- 透光率 [%]: 96.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.7 MPa | 1550 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.3 MPa | 1500 psi | ASTM D882 |
| Film Elongation at Break, MD | 480 % | 480 % | ASTM D882 |
| Film Elongation at Break, TD | 740 % | 740 % | ASTM D882 |
| Secant Modulus, MD | 0.129621 GPa | 18.8003 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.122037 GPa | 17.7003 ksi | 2% Secant; ASTM D882 |
| Impact | 488 | 488 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 2800 | 2800 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 3300 | 3300 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 260 g | 260 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 400 g | 400 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 12.8 g/micron | 325 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 19.7 g/micron | 500 g/mil | ASTM D1922 |
| Dart drop Test | 594 g | 1.31 lb | Method B; ASTM D1709 |
| Film Tensile Strength at Break, MD | 62.4 MPa | 9050 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 48.3 MPa | 7000 psi | ASTM D882 |
| Heat Seal Strength Initiation Temperature | 95.0 °C | 203 °F | 1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 122 °C | 252 °F | Dow Method (DSC) |
| Vicat Softening Point | 88.0 °C | 190 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.5 % | 9.5 % | ASTM D1003 |
| Gloss | 55 % | 55 % | 45°; ASTM D2457 |
| Transmission, Visible | 96 % | 96 % | Clarity; ASTM D1746 |