- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.928
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.928 g/cc | 0.0335 lb/in3 | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 14.58 MPa | 2115 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 14.60 MPa | 2118 psi | ASTM D882 |
| Film Elongation at Break, MD | 606 % | 606 % | ASTM D882 |
| Film Elongation at Break, TD | 780 % | 780 % | ASTM D882 |
| Secant Modulus, MD | 0.246998 GPa | 35.8246 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.275128 GPa | 39.9046 ksi | 2% Secant; ASTM D882 |
| Impact | 32 | 32 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 2532 | 2532 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 2640 | 2640 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 379 g | 379 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 449 g | 449 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 7.461 g/micron | 189.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 8.839 g/micron | 224.5 g/mil | ASTM D1922 |
| Dart drop Test | 89.0 g | 0.196 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 24.24 MPa | 3515 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 21.04 MPa | 3051 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.2 % | 7.2 % | ASTM D1003 |
| Gloss | 77 % | 77 % | 45°; ASTM D2457 |