- 密度 [g/cm3]: 0.884
- 彎曲模量 [MPa]: 0.0331
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.884 g/cc | 0.0319 lb/in3 | ASTM D792 |
| High Load Melt Index | 4.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 4.0 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Melt Index of Compound | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 83 | 83 | 1 sec; molded and tested in accordance with ASTM D4976; ASTM D2240 |
| 83 | 83 | 5 sec; molded and tested in accordance with ASTM D4976; ASTM D2240 | |
| Tensile Strength at Break | 4.83 MPa | 700 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 300 % | 300 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 0.0331 GPa | 4.80 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 114 °C | 237 °F | Dow Method (DSC) |
| Glass Transition Temp, Tg | -48.9 °C | -56.0 °F | Dow Method |