- 熔體流動速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.913
- 拉伸強度 [MPa]: 8.0
- 彎曲強度 [MPa]: 8.0
- 脆化溫度 [℃]: -45.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.913 - 1.19 g/cc | 0.0330 - 0.0430 lb/in3 | Average value: 0.939 g/cc Grade Count:30 |
| Volatiles | 0.200 % | 0.200 % | Average value: 0.200 % Grade Count:3 |
| Particle Size | 150 - 1200 μm | 150 - 1200 μm | Average value: 404 μm Grade Count:27 |
| Carbon Black Loading | 30.0 - 43.0 % | 30.0 - 43.0 % | Average value: 36.5 % Grade Count:3 |
| Melt Flow | 0.200 - 155 g/10 min | 0.200 - 155 g/10 min | Average value: 48.4 g/10 min Grade Count:28 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 40.0 - 50.0 | 40.0 - 50.0 | Average value: 44.2 Grade Count:17 |
| Tensile Strength, Ultimate | 8.00 - 9.00 MPa | 1160 - 1310 psi | Average value: 8.50 MPa Grade Count:4 |
| Tensile Strength, Yield | 8.00 - 9.00 MPa | 1160 - 1310 psi | Average value: 8.50 MPa Grade Count:4 |
| Elongation at Break | 90.0 - 100 % | 90.0 - 100 % | Average value: 97.1 % Grade Count:21 |
| Modulus of Elasticity | 0.0900 - 0.200 GPa | 13.1 - 29.0 ksi | Average value: 0.124 GPa Grade Count:13 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 100 - 140 °C | 212 - 284 °F | Average value: 107 °C Grade Count:27 |
| Vicat Softening Point | 68.0 - 92.0 °C | 154 - 198 °F | Average value: 78.1 °C Grade Count:27 |
| Brittleness Temperature | -45.0 - -25.0 °C | -49.0 - -13.0 °F | Average value: -35.0 °C Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 200 °C | 392 °F | Average value: 200 °C Grade Count:8 |