- 熔體流動速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.917
- 拉伸強度 [MPa]: 8.34
- 彎曲強度 [MPa]: 9.0
- 彎曲模量 [MPa]: 0.125
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 - 2.00 g/cc | 0.0331 - 0.0723 lb/in3 | Average value: 0.998 g/cc Grade Count:62 |
| Volatiles | 0.0700 - 0.100 % | 0.0700 - 0.100 % | Average value: 0.0850 % Grade Count:4 |
| Environmental Stress Crack Resistance | 1.00 - 1000 hour | 1.00 - 1000 hour | Average value: 211 hour Grade Count:39 |
| >= 96.0 hour @Temperature 50.0 - 50.0 °C | >= 96.0 hour @Temperature 122 - 122 °F | Average value: 1150 hour Grade Count:4 | |
| Melt Flow | 0.200 - 12.0 g/10 min | 0.200 - 12.0 g/10 min | Average value: 1.44 g/10 min Grade Count:66 |
| Degree of Crosslinking | 12.0 % | 12.0 % | Average value: 12.0 % Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 44.0 - 53.0 | 44.0 - 53.0 | Average value: 47.7 Grade Count:17 |
| Tensile Strength, Ultimate | 9.00 - 25.0 MPa | 1310 - 3630 psi | Average value: 12.8 MPa Grade Count:13 |
| Tensile Strength, Yield | 8.34 - 20.7 MPa | 1210 - 3000 psi | Average value: 12.6 MPa Grade Count:44 |
| Elongation at Break | 50.0 - 900 % | 50.0 - 900 % | Average value: 379 % Grade Count:55 |
| Elongation at Yield | 14.0 - 50.0 % | 14.0 - 50.0 % | Average value: 44.9 % Grade Count:7 |
| Flexural Modulus | 0.125 - 0.300 GPa | 18.1 - 43.5 ksi | Average value: 0.208 GPa Grade Count:7 |
| Tear Strength Test | 13.7 - 115 | 13.7 - 115 | Average value: 25.0 Grade Count:9 |
| Tensile Set | 5.00 - 360 % | 5.00 - 360 % | Average value: 24.7 % Grade Count:17 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+6 - 1.00e+18 ohm-cm | 1.00e+6 - 1.00e+18 ohm-cm | Average value: 4.42e+16 ohm-cm Grade Count:27 |
| Dielectric Constant | 2.03 - 2.70 | 2.03 - 2.70 | Average value: 2.34 Grade Count:63 |
| Dielectric Strength | 2.17 - 49.6 kV/mm | 55.0 - 1260 kV/in | Average value: 31.3 kV/mm Grade Count:58 |
| Dissipation Factor | 0.0000100 - 0.00700 | 0.0000100 - 0.00700 | Average value: 0.000722 Grade Count:59 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 104 - 110 °C | 219 - 230 °F | Average value: 108 °C Grade Count:6 |
| Maximum Service Temperature, Air | 15.0 °C | 59.0 °F | Average value: 15.0 °C Grade Count:8 |
| Brittleness Temperature | -76.0 - -67.0 °C | -105 - -88.6 °F | Average value: -74.1 °C Grade Count:12 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 240 °C | 176 - 464 °F | Average value: 150 °C Grade Count:6 |
| Die Temperature | 141 - 185 °C | 285 - 365 °F | Average value: 174 °C Grade Count:10 |
| Melt Temperature | 120 - 230 °C | 248 - 446 °F | Average value: 162 °C Grade Count:13 |
| Head Temperature | 140 - 185 °C | 284 - 365 °F | Average value: 174 °C Grade Count:10 |