- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in3 | ASTM D1505 | ||
| Thickness | 32.0 microns | 1.26 mil | 2:1 blow-up ratio | ||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 15.2 MPa | 2200 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 12.4 MPa | 1800 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 360 % | 360 % | ASTM D-882 | ||
| Film Elongation at Break, TD | 580 % | 580 % | ASTM D-882 | ||
| Secant Modulus, MD | 0.193 GPa | 28.0 ksi | value @ 0.1 mm/mm-min Initial strain rate; ASTM D-882 | ||
| Secant Modulus, TD | 0.207 GPa | 30.0 ksi | value @ 0.1 mm/mm-min Initial strain rate; ASTM D-882 | ||
| Elmendorf Tear Strength, MD | 17.7 g/micron | 450 g/mil | ASTM D-1922 | ||
| Elmendorf Tear Strength, TD | 8.30 g/micron | 211 g/mil | ASTM D-1922 | ||
| Dart Drop | 2.46 g/micron | 62.5 g/mil | 26 in. dart; ASTM D-1709, A | ||
| Film Tensile Strength at Break, MD | 0.157 MPa | 22.8 psi | ASTM D-882 | ||
| Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D-882 | ||
| Optical Properties | Metric | English | Comments | ||
| Gloss | 67 % | 67 % | ASTM D-2457 | ||
| Descriptive Properties | |||||
| process | Film | ||||