- 熔體流動速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.918
- 拉伸強度 [MPa]: 8.48
- 彎曲強度 [MPa]: 10.3
- 彎曲模量 [MPa]: 0.152
- 熱變形溫度 [℃]: 40.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 - 0.955 g/cc | 0.0332 - 0.0345 lb/in3 | Average value: 0.923 g/cc Grade Count:39 |
| Apparent Bulk Density | 0.526 g/cc | 0.0190 lb/in3 | Average value: 0.526 g/cc Grade Count:3 |
| Environmental Stress Crack Resistance | 16.0 - 100 hour | 16.0 - 100 hour | Average value: 72.0 hour Grade Count:3 |
| Thickness | 31.8 - 50.8 microns | 1.25 - 2.00 mil | Average value: 34.9 microns Grade Count:4 |
| Melt Flow | 0.250 - 22.0 g/10 min | 0.250 - 22.0 g/10 min | Average value: 2.50 g/10 min Grade Count:40 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 47.0 - 59.0 | 47.0 - 59.0 | Average value: 51.7 Grade Count:19 |
| Tensile Strength, Ultimate | 10.3 - 18.0 MPa | 1500 - 2610 psi | Average value: 13.9 MPa Grade Count:24 |
| Tensile Strength, Yield | 8.48 - 26.2 MPa | 1230 - 3800 psi | Average value: 13.0 MPa Grade Count:22 |
| Film Elongation at Break, MD | 200 - 230 % | 200 - 230 % | Average value: 216 % Grade Count:3 |
| Film Elongation at Break, TD | 500 - 610 % | 500 - 610 % | Average value: 548 % Grade Count:3 |
| Elongation at Break | 100 - 700 % | 100 - 700 % | Average value: 526 % Grade Count:28 |
| Modulus of Elasticity | 0.180 - 0.483 GPa | 26.1 - 70.1 ksi | Average value: 0.318 GPa Grade Count:10 |
| Flexural Modulus | 0.152 - 2.21 GPa | 22.0 - 320 ksi | Average value: 0.366 GPa Grade Count:18 |
| Secant Modulus, MD | 0.152 - 0.208 GPa | 22.0 - 30.2 ksi | Average value: 0.177 GPa Grade Count:4 |
| Secant Modulus, TD | 0.172 - 0.228 GPa | 25.0 - 33.0 ksi | Average value: 0.193 GPa Grade Count:3 |
| Elmendorf Tear Strength MD | 270 - 390 g | 270 - 390 g | Average value: 306 g Grade Count:3 |
| Elmendorf Tear Strength TD | 100 - 170 g | 100 - 170 g | Average value: 152 g Grade Count:3 |
| Dart drop Test | 65.0 - 120 g | 0.143 - 0.265 lb | Average value: 95.0 g Grade Count:4 |
| Film Tensile Strength at Break, MD | 18.6 - 29.1 MPa | 2700 - 4220 psi | Average value: 24.0 MPa Grade Count:3 |
| Film Tensile Strength at Break, TD | 17.0 - 17.9 MPa | 2470 - 2600 psi | Average value: 17.3 MPa Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 40.0 - 54.0 °C | 104 - 129 °F | Average value: 47.0 °C Grade Count:7 |
| Vicat Softening Point | 85.0 - 107 °C | 185 - 225 °F | Average value: 94.7 °C Grade Count:28 |
| Brittleness Temperature | -76.0 - 0.500 °C | -105 - 32.9 °F | Average value: -67.5 °C Grade Count:10 |
| Optical Properties | Metric | English | Comments |
| Haze | 3.40 - 15.0 % | 3.40 - 15.0 % | Average value: 8.45 % Grade Count:6 |
| Gloss | 20.0 - 77.0 % | 20.0 - 77.0 % | Average value: 60.2 % Grade Count:6 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 160 - 260 °C | 320 - 500 °F | Average value: 196 °C Grade Count:11 |