- 熔體流動速率 [g/10min]: 0.18
- 密度 [g/cm3]: 0.915
- 拉伸強度 [MPa]: 7.6
- 彎曲強度 [MPa]: 9.0
- 彎曲模量 [MPa]: 0.0800
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.915 - 0.939 g/cc | 0.0331 - 0.0339 lb/in3 | Average value: 0.920 g/cc Grade Count:73 |
| Moisture Vapor Transmission | 0.410 - 0.410 cc-mm/m2-24hr-atm @Temperature 37.8 - 37.8 °C | 1.04 - 1.04 cc-mil/100 in2-24hr-atm @Temperature 100 - 100 °F | Average value: 0.410 cc-mm/m2-24hr-atm Grade Count:1 |
| 0.410 - 0.410 cc-mm/m2-24hr-atm @Thickness 0.0254 - 0.0254 mm | 1.04 - 1.04 cc-mil/100 in2-24hr-atm @Thickness 0.00100 - 0.00100 in | Average value: 0.410 cc-mm/m2-24hr-atm Grade Count:1 | |
| Water Vapor Transmission | 0.260 - 20.0 g/m2/day | 0.0167 - 1.29 g/100 in2/day | Average value: 15.8 g/m2/day Grade Count:10 |
| Environmental Stress Crack Resistance | 18.0 - 10000 hour | 18.0 - 10000 hour | Average value: 2410 hour Grade Count:5 |
| Oxidative Induction Time (OIT) | >= 40.0 min @Temperature 200 - 200 °C | >= 40.0 min @Temperature 392 - 392 °F | Average value: 40.0 min Grade Count:1 |
| Thickness | 25.0 - 150 microns | 0.984 - 5.91 mil | Average value: 54.3 microns Grade Count:24 |
| Melt Flow | 0.180 - 16.0 g/10 min | 0.180 - 16.0 g/10 min | Average value: 5.72 g/10 min Grade Count:59 |
| Base Resin Melt Index | 0.330 - 7.00 g/10 min | 0.330 - 7.00 g/10 min | Average value: 2.98 g/10 min Grade Count:14 |
| Neck In | 3.60 - 9.00 cm | 1.42 - 3.54 in | Average value: 4.86 cm Grade Count:9 |
| Drawdown | 1.07 - 9.10 m/s | 210 - 1790 ft/min | Average value: 4.39 m/s Grade Count:7 |
| Coating Weight | 6.40 - 9.60 g/m2 | 4.00 - 6.00 lb/ream | Average value: 8.00 g/m2 Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 42.0 - 57.0 | 42.0 - 57.0 | Average value: 49.0 Grade Count:22 |
| Tensile Strength, Ultimate | 9.00 - 18.0 MPa | 1310 - 2610 psi | Average value: 11.6 MPa Grade Count:29 |
| Tensile Strength, Yield | 7.60 - 12.0 MPa | 1100 - 1740 psi | Average value: 9.90 MPa Grade Count:22 |
| Film Elongation at Break, MD | 190 - 490 % | 190 - 490 % | Average value: 297 % Grade Count:31 |
| Film Elongation at Break, TD | 220 - 900 % | 220 - 900 % | Average value: 519 % Grade Count:31 |
| Elongation at Break | 226 - 650 % | 226 - 650 % | Average value: 537 % Grade Count:29 |
| Modulus of Elasticity | 0.152 - 0.290 GPa | 22.0 - 42.1 ksi | Average value: 0.204 GPa Grade Count:9 |
| Flexural Modulus | 0.0800 - 0.276 GPa | 11.6 - 40.0 ksi | Average value: 0.209 GPa Grade Count:12 |
| Secant Modulus, MD | 0.0830 - 1.28 GPa | 12.0 - 185 ksi | Average value: 0.232 GPa Grade Count:19 |
| Secant Modulus, TD | 0.124 - 1.18 GPa | 18.0 - 171 ksi | Average value: 0.254 GPa Grade Count:19 |
| Elmendorf Tear Strength MD | 250 - 600 g | 250 - 600 g | Average value: 465 g Grade Count:10 |
| Elmendorf Tear Strength TD | 55.0 - 500 g | 55.0 - 500 g | Average value: 284 g Grade Count:12 |
| Elmendorf Tear Strength, MD | 2.50 - 12.0 g/micron | 63.5 - 305 g/mil | Average value: 8.19 g/micron Grade Count:21 |
| Elmendorf Tear Strength, TD | 2.20 - 7.00 g/micron | 55.9 - 178 g/mil | Average value: 4.71 g/micron Grade Count:22 |
| Dart Drop | 2.00 - 11.0 g/micron | 50.8 - 279 g/mil | Average value: 3.48 g/micron Grade Count:24 |
| Dart drop Test | 64.0 - 650 g | 0.141 - 1.43 lb | Average value: 212 g Grade Count:13 |
| Hot Tack Strength | 225 g/25 mm | 225 g/in | Average value: 225 g/25 mm Grade Count:3 |
| Film Tensile Strength at Break, MD | 11.0 - 78.5 MPa | 1600 - 11400 psi | Average value: 23.6 MPa Grade Count:31 |
| Film Tensile Strength at Break, TD | 10.0 - 53.9 MPa | 1450 - 7820 psi | Average value: 18.9 MPa Grade Count:31 |
| Heat Seal Strength | 1400 g/25 mm | 3.09 lb/in | Average value: 1400 g/25 mm Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.27 - 2.29 | 2.27 - 2.29 | Average value: 2.28 Grade Count:4 |
| Dissipation Factor | 0.0000400 - 0.000100 | 0.0000400 - 0.000100 | Average value: 0.0000633 Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 104 - 113 °C | 219 - 235 °F | Average value: 108 °C Grade Count:7 |
| Vicat Softening Point | 84.0 - 128 °C | 183 - 262 °F | Average value: 91.9 °C Grade Count:44 |
| Brittleness Temperature | -76.0 - -60.0 °C | -105 - -76.0 °F | Average value: -72.8 °C Grade Count:5 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.00 - 17.0 % | 5.00 - 17.0 % | Average value: 7.90 % Grade Count:21 |
| Gloss | 10.0 - 78.0 % | 10.0 - 78.0 % | Average value: 59.2 % Grade Count:13 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 200 - 340 °C | 392 - 644 °F | Average value: 275 °C Grade Count:3 |
| Feed Temperature | 138 - 163 °C | 280 - 325 °F | Average value: 151 °C Grade Count:4 |
| Adapter Temperature | 204 - 221 °C | 400 - 430 °F | Average value: 213 °C Grade Count:4 |
| Die Temperature | 204 - 221 °C | 400 - 430 °F | Average value: 213 °C Grade Count:4 |
| Melt Temperature | 107 - 327 °C | 225 - 620 °F | Average value: 206 °C Grade Count:47 |
| Blow-up Ratio (BUR) | 1.50 - 3.00 | 1.50 - 3.00 | Average value: 2.16 Grade Count:22 |