- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.92
- 拉伸強度 [MPa]: 10.0
- 彎曲模量 [MPa]: 0.179
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in3 | ASTM D-1505 | ||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 47 | 47 | ASTM D-2240 | ||
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D-638 | ||
| Elongation at Break | 600 % | 600 % | ASTM D-638 | ||
| Modulus of Elasticity | 0.186 GPa | 27.0 ksi | ASTM D-638 | ||
| Flexural Modulus | 0.179 GPa | 26.0 ksi | ASTM D-790 | ||
| Izod Impact, Notched | NB | NB | ASTM D-256 | ||