| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Base Resin Density | 0.920 g/cc | 0.0332 lb/in3 | ASTM D1505 |
| Thickness | 25.0 microns | 0.984 mil | slot cast film at 280°C |
| Base Resin Melt Index | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| 1% Secant Modulus | 225.56 MPa | 32714 psi | Base Resin; ASTM D638 |
| Dart Drop | 4.00 g/micron | 102 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 36.3 MPa | 5260 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 26.5 MPa | 3840 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.6 % | 1.6 % | ASTM D1003 |
| Gloss | 90 % | 90 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 200 - 280 °C | 392 - 536 °F | |